The Bambu Lab PLA Wood Filament is a 1.75 mm composite PLA infused with wood particles to deliver authentic wood-like texture and finish straight off the printer. With balanced mechanical properties, defined printing parameters, and natural aesthetics, it’s perfect for decorative parts, props, and artisan-style 3D prints.

Filament With Spool

Bambu Lab 3D Printer Filaments | PLA Wood w Reusable Spool

Style: Classic Birch
SKU: BAM-A16-G0-1.75-1000-SPL
Cart Share
  • Real Wood-Like Texture – PLA blended with wood particles delivers natural wood grain aesthetics and surface feel.
  • Standard 1.75mm Diameter – Precision 1.75 mm filament ensures consistent extrusion on compatible FDM printers.
  • Warm Print Finish – Unique composite formulation produces warm, organic tones compared to regular PLA.
  • Defined Printing Temperature Range – Official recommended nozzle and bed temperatures ensure reliable adhesion and surface quality.
  • Balanced Mechanical Properties – Detailed tensile, bending, and impact strength values support confident functional and decorative design decisions.
  • Humidity & Drying Control – Includes guidelines for storing and drying wood composite filaments to maintain performance.
  • Wide Nozzle Support – Supports multiple nozzle sizes, offering options for detail (smaller nozzles) or faster flow (larger nozzles).
  • Thermal Performance Data – Key thermal properties like glass transition and heat deflection temperatures are specified for design insight.
SpecificationDetails
Product NameBambu Lab PLA Wood Filament
Filament TypePLA Wood Composite
Diameter1.75mm
Net Filament Weight1kg
Spool MaterialABS (Temperature resistance 70°C)
Spool SizeDiameter: 200mm
Height: 67mm
Nozzle Temperature190–230°C
Bed Temperature35–45°C
Printing Speed< 250mm/s
Cooling FanOn
Drying SettingsBlast drying oven ~55°C for 8h
Heatbed ~65–75°C for 12h
Humidity (Storage/Printing)< 20% RH (sealed with desiccant)
Glass Transition Temperature~57°C
Vicat Softening Temperature~61°C
Heat Deflection Temperature~60–63°C
Density~1.22g/cm³
Tensile Strength (X-Y)~31–35MPa
Tensile Strength (Z)~28–31MPa
Bending Modulus (X-Y)~2300–2600MPa
Bending Modulus (Z)~1900–2400MPa
Bending Strength (X-Y)~70–78MPa
Bending Strength (Z)~50–58MPa
Impact Strength (X-Y)~20–30kJ/m²
Impact Strength (Z)~7–12kJ/m²
Printer Compatibility (for filaments / printer accessories)Compatible with FDM printers that support 1.75mm filaments.
In the Box / What’s IncludedPLA Wood filament on reusable spool