Name: Bambu Lab 3D Printer Filaments | PLA Silk+ w Reusable Spool
Brand: Bambu Lab
SKU: BAM-A05-T4-1.75-1000-SPL
Price: 31.9 SGD
Availability: InStock

1/9

SGD $31.90

The Bambu Lab PLA Silk+ is a 1.75 mm filament that delivers strong mechanical performance with a stunning silk gloss finish. Engineered for smooth, consistent extrusion and visual appeal, it’s ideal for decorative prints, prototypes, and functional parts where shine and strength matter.

Filament With Spool

Style: Blue Hawaii (Blue-Green)

Variant

Quantity:

SKU: BAM-A05-T4-1.75-1000-SPL

Silk Gloss Surface Finish – Designed to deliver a smooth, lustrous shine for premium-looking 3D prints.
Standard 1.75mm Filament Diameter – Manufactured in 1.75mm size for consistent extrusion on compatible FDM printers.
Defined Printing Temperature Range – Recommended nozzle temperature is 210–240°C for stable flow and surface quality.
Controlled Bed Temperature Range – Recommended bed temperature is 35–45°C for reliable first-layer adhesion.
High-Speed Printing Capability – Rated for printing speeds below 250mm/s for efficient output.
Multi-Nozzle Compatibility – Supports nozzle sizes from 0.2mm to 0.8mm for detailed or high-flow printing.
Drying & Storage Guidelines – Recommended drying and humidity control are specified to maintain filament quality.
Detailed Mechanical & Thermal Data – Official tensile, bending, impact, and heat resistance properties are provided for design reference.

Specification	Details
Product Name	Bambu Lab PLA Silk+
Filament Type	PLA Silk+
Diameter	1.75mm
Net Filament Weight	1kg
Spool Material	ABS (Temperature resistance 70°C)
Spool Size	Diameter: 200mm Height: 67mm
Nozzle Temperature	210–240°C
Bed Temperature	35–45°C
Printing Speed	< 250mm/s
Cooling Fan	On
Recommended Drying Settings	Blast drying oven: 55°C, 8h X1 Series heatbed: 65–75°C, 12h
Humidity (Printing/Storage)	< 20% RH (sealed with desiccant)
Nozzle Sizes Supported	0.2mm, 0.4mm, 0.6mm, 0.8mm
Physical Density	1.27g/cm³
Glass Transition Temperature	57°C
Vicat Softening Temperature	66°C
Heat Deflection Temperature	56–60°C
Tensile Strength (X-Y)	33 ± 4MPa
Tensile Strength (Z)	25 ± 4MPa
Young’s Modulus (X-Y)	2130 ± 210MPa
Young’s Modulus (Z)	1850 ± 140MPa
Bending Strength (X-Y)	75 ± 4MPa
Bending Strength (Z)	30 ± 5MPa
Impact Strength (X-Y)	18.5 ± 1.6kJ/m²
Impact Strength (Z)	8.5 ± 1.1kJ/m²
Saturated Water Absorption	0.40% (25°C, 55% RH)
Chemical Stability & Resistance	Stable under normal conditions Resistant to most oil & grease Not resistant to acid/alkali/organic solvents